| by IDEX Health & Science In contrast, Semrock manufacturers all of its optical filters with a deposition process called sputtering. This state-of-the-art technology was originally developed for coating precise ferrite thin films for magnetic disk drive heads, and then gained a reputation in the optics arena for fabrication of extremely low-loss mirrors for ring-laser gyroscope applications. In the late-1990’s it was adapted to manufacture the highest-performance optical filters for wavelength-division multiplexing in the booming fiber-optic telecommunications industry. Sputtering produces hard refractory oxide thin films – as hard as the glass substrates on which they are coated. This stable process is renowned for its ability to reproducibly deposit many hundreds of low-loss, reliable thin-film layers with high optical-thickness precision. One way to clearly see the difference among soft evaporated films, the more robust films produced with IAD, and the very dense, low-scattering films resulting from the sputtering process is to study the film surface morphology closely. Atomic force microscopy reveals surface characteristics indicative of the packing density of the films. The graph below shows results from a study that compared the three main deposition methods as well as two other less-common modified processes [1]. Films were coated on substrates with a starting root-mean-square (RMS) surface roughness below 0.5 Å. Only sputtering produces highly multi-layered films with sufficient packing density to result in surface roughness comparable to that of the starting substrate. A perceived limitation of the sputtering process has always been throughput – the excellent performance came at the expense of slow deposition rates and limited coating areas. For the established applications of disk drive heads and telecom filters with dimensions of only one to several mm at most this limitation was not too severe. However, it was considered a show-stopper for costeffective production of larger filters in higher volumes. Semrock broke through this limitation by turning sputtering into a true high-volume manufacturing platform for large (dimensions of inches) very high layer count optical filters. And we did this without compromising the optical performance for which sputtering was renowned, resulting from dense, low-scattering thin film layers of extreme optical-thickness precision. Semrock made ground-breaking developments in process technology to boost rates and uniformity, and we are continually improving the process even today. And our highly advanced deposition-control technology based on the proprietary hardware, algorithms, and software of Semrock’s “optical monitoring” system enables repeatable deposition of many hundreds of thin film layers of even arbitrary thickness for complex filters with superb spectral features. [1] “Optical Morphology: Just How Smooth Is That Surface?,” C. Langhorn and A. Howe, Photonics Spectra (Laurin Publishing), June 1998.