LIGHT-EMITTING DIODES: Microlens arrays improve the extraction efficiency of nitride LEDs

The light-extraction efficiency of quantum-well (QW) light-emitting diodes (LEDs) is one of the keys to the quantum efficiency of these devices.

Jan 1st, 2008
Th 0801lfwnews14f1

The light-extraction efficiency of quantum-well (QW) light-emitting diodes (LEDs) is one of the keys to the quantum efficiency of these devices. In III-nitride devices, the large refractive-index difference between the gallium nitride and air poses a problem. Numerous attempts to improve light-extraction efficiency of nitride quantum-well LEDs have not been successful in terms of cost, process control, or scalable production. Now, an inexpensive new approach using microlens arrays on top of the quantum-well structure has led to a significant increase in extraction efficiency, and is simple to control and scalable, say researchers at Lehigh University (Bethlehem, PA).1

A team of optical and materials engineers led by assistant professor Nelson Tansu created the microlens array directly on top of an indium gallium nitride (InGaN) QW LED device. Uniform microspheres in colloidal suspension tend to spontaneously create a two-dimensional crystal, so the rapid convective deposition of a monolayer of polystyrene (PS) microspheres directly onto the top of LED structure is “practical and straightforward,” according to the researchers. A second layer of silicon dioxide (SiO2) was then flowed on top of the PS layer and heated to 140°C. This process melted the PS microspheres, forming a close-packed layer of hexagonal, lenslike arrays (see Fig. 1).

FIGURE 1. A colloidal SiO2/polystyrene crystal forms a two-dimensional microlens array on top of an InGaN QW LED structure, to more than double the extraction efficiency of the device. (Courtesy of Lehigh University)
Click here to enlarge image

The use of SiO2/polystyrene microlens arrays on the top surface of the LED allows the photons emanating from the QW to scatter away from the structure with a larger effective “photon escape cone,” leading to increased light-extraction efficiency. In addition, the reduced refractive indices of SiO2 (n = 1.46) and polystyrene (n = 1.58) in the microlens arrays leads to reduced Fresnel reflection at the interface of the air, GaN, and microlens array. The photoluminescence (PL) peak intensity of the samples at λpeak = 419.3 nm exhibited a 233.6% improvement with the microlenses than without (see Fig. 2). The integrated photoluminescence for samples covered with the array showed an improvement of 269% over the uncoated sample. And at 480 nm, output is improved by 219% with use of the microlens arrays.

FIGURE 2. The photoluminescence intensity of InGaN QW LEDs shows more than a 200% improvement with the deposition of a SiO2/polystyrene microlens layer, excited by a helium-cadmium 325 nm laser at room temperature.
Click here to enlarge image

At low current levels of 5 mA, the relative external quantum efficiency of the LEDs was improved 4.34 times with the SiO2/PS layer. For 100 mA, the improvement was 3.32 times that of LEDs with no microlens arrays on top.

Further understanding is required, and the Lehigh group will continue to research better light-extraction efficiency of the QW LEDs. “We plan to conduct comprehensive modeling and parametric studies to optimize the sphere diameters and the PS layer thickness, and to optimize the fabrication of the arrays,” says Tansu.

Valerie C. Coffey


1. Y. Ee et al., Appl. Phys. Lett. 91, 221107 (Nov. 26, 2007).